Black Chromia Coatings on Metal Tubes for the Solar Collectors
Brožek, V. ; Mastný, L. ; Novák, M. ; Vilémová, Monika ; Kubatík, Tomáš František
This paper describes the results of the first phase of the study preparation, structure and properties of coatings modification of black chromium oxide on copper, aluminium, iron and zirconium tubes for solar collectors. The coatings are prepared by plasma spraying of liquid chromate method which is known as liquid precursor plasma spraying. Coatings have the function of an energy trap for thermal radiation wavelengths of 1 μm – 3 μm i.e. in the IR region. At the same time, the coating increases the corrosion resistance of metal substrates. The nanometric structure and thickness of the coating depend of the feeding distance and the concentration of chromate precursors. For the deposition of nanometric splats of melt chromiumIII oxide, a new type of feeder that injects precursors into the water stabilized thermal plasma produced by the WSP® generator has been\ndeveloped.\n
|
|
|
Black Chromia Plating for the Solar Radiation Absorbers
Brožek, Vlastimil ; Březina, Václav ; Brom, Petr ; Kubatík, Tomáš František ; Vilémová, Monika ; Mastný, L. ; Novák, M.
Black chromia layers were produced on copper, zirconium and aluminium substrates. These layers are aimed to serve as solar collectors. Efficiency of the layers during UV-VIS, UV radiation and WSP® plasma torch radiation is described. The chromia layers were prepared by a new procedure, i.e. deposition of ammonium dichromate solution using plasma torch or so called Liquid Precursor Plasma Spraying (LPPS). Solution of ammonium dichromate is fed into plasma stream, where dissociation takes place under temperatures of 4000 K – 25000 K. Up to nanometric oxide particles can be produced; the resulting size is dependent on solution concentration and feeding nozzle diameter. The particles impact on substrate and form coating. Using 2 wt.% to 5 wt.% solution of ammonium dichromate and feeding nozzle of 0.2 mm in diameter is the size of produced chromia particles about 6 µm which results in formation of 2 µm to 3 µm thick coating, i.e. according to the theory an optimal thickness 2.5 um for absorption layers, necessary condition for formation energy traps for IR radiation emitters up to 100°C. Moreover, black chromia coating is a suitable corrosion barrier of metallic substrates. \n\n
|
guest ::